PolyJet 3D Printing
PolyJet 3D printing is an excellent technology for quickly manufacturing high-resolution products in a range of colors with glossy or matte finishes. Plastics printed with PolyJet have a smooth, high-quality finish. As a result, PolyJet prototypes and models are very useful for approximating final products with intricate details and delicate features. Because they are made from real thermoplastics, PolyJet parts can be either hard or rubbery.
3D printed plastics are strong, inexpensive and quick to produce. They also eliminate many of the design restrictions of traditional manufacturing. To learn more about our other plastic 3D printing options, check out our HP Multi Jet Fusion 3D printing services or our 5-Minute Buyer’s Guide.
PolyJet 3D Printing, On Demand
Get a quote that works for you with our Instant Quote and Classic Quote tools. Instantly quote and order 3D printed parts for Multi Jet Fusion, FDM, PolyJet, ColorJet and Direct Metal with Instant Quote, or use Classic Quote to get a quote in under 24 hours for all of our manufacturing and engineering services!
PolyJet Design Guidelines
Please note that these are guidelines, not hard-and-fast rules. Follow these, and you should be in pretty good shape. We’ll let you know if we see any problems with your design.
PolyJet (Objet) Basic Materials Data Sheet
PolyJet (Objet) Digital Materials Data Sheet
| Parameter | Inches | Milimeters |
| Minimum Supported Wall Thickness | 0.030 | 0.75 |
| Minimum Unsupported Wall Thickness | 0.040 | 1.00 |
| Minimum Supported Bosses | 0.030 | 0.75 |
| Minimum Unsupported Bosses | 0.040 | 1.00 |
| Minimum Embossed Detail (Height and Width) | 0.010 | 0.25 |
| Minimum Engraved Detail (Height and Width) | 0.010 | 0.25 |
| Clearance | 0.010 | 0.25 |
Standard Material Properties
This data is provided for the convenience of our customers. It does not on its own represent a sufficient basis for any part design, nor does it provide any agreement about or guarantee the specific properties of a product or part or the suitability of a product or part for a specific application. It is the responsibility of the producer or customer of a part to check its properties as well as its suitability for a particular purpose. This also applies to any possible intellectual property rights as well as regional laws and regulations. The data are subject to change without notice.
Durus White (Polypropylene-like Material)
| Property | Value | Units |
| Tensile Strength | 2900-4350 | psi |
| Elongation at Break | 40-50 | % |
| Elastic Modulus | 145,000-175,000 | psi |
| Flexural Strength | 4350-5800 | psi |
| Flexural Modulus | 175,000-230,000 | psi |
| HDT @ 65 psi | 99-108 | °F |
| HDT @ 265 psi | 90-93 | °F |
| Izod Notched Impact | 0.749-0.937 | ft lb/inch |
| Water Absorption | 1.5-1.9 | % |
| Glass Transition | 95-99 | °F |
| Shore Hardness | 74-78 | D |
| Rockwell Hardness | No Data | Scale M |
| Polymerized Density | 1.15-1.17 | g/cm3 |
| Ash Content | 0.10-0.12 | % |
VeroWhite (Acrylic)
| Property | Value | Units |
| Tensile Strength | 7250-9450 | psi |
| Elongation at Break | 10-25 | % |
| Elastic Modulus | 290,000-435,000 | psi |
| Flexural Strength | 11,000-16,000 | psi |
| Flexural Modulus | 320,000-465,000 | psi |
| HDT @ 65 psi | 113-122 | °F |
| HDT @ 265 psi | 113-122 | °F |
| Izod Notched Impact | 0.375-0.562 | ft lb/inch |
| Water Absorption | 1.1-1.5 | % |
| Glass Transition | 126-129 | °F |
| Shore Hardness | 83-86 | D |
| Rockwell Hardness | 73-76 | Scale M |
| Polymerized Density | 1.17-1.18 | g/cm3 |
| Ash Content | 0.01-0.02 | % |
VeroClear (Acrylic)
| Property | Value | Units |
| Tensile Strength | 7250-9450 | psi |
| Elongation at Break | 10-25 | % |
| Elastic Modulus | 290,000-435,000 | psi |
| Flexural Strength | 11,000-16,000 | psi |
| Flexural Modulus | 320,000-465,000 | psi |
| HDT @ 65 psi | 113-122 | °F |
| HDT @ 265 psi | 113-122 | °F |
| Izod Notched Impact | 0.375-0.562 | ft lb/inch |
| Water Absorption | 1.1-1.5 | % |
| Glass Transition | 126-129 | °F |
| Shore Hardness | 83-86 | D |
| Rockwell Hardness | 73-76 | Scale M |
| Polymerized Density | 1.18-1.19 | g/cm3 |
| Ash Content | 0.02-0.06 | % |